Product Description
The Z150 in the DX51D Z150 galvanized coil is the actual coating name. The manufacturer describes the DX51D Z150 material as a mild steel galvanized layer for steel products. Specifically, DX51D is a steel grade characterized by its cold-formed bending and profiling qualities. Galvanized coil is made of a type of steel that is coated with zinc for protection by an electroplating process. The galvanized layer is applied to cold rolled steel at low temperatures. Zinc is generally represented by Z. Z is the abbreviation of English Zinc. For example, the Z80 surface zinc plating content is 80 grams per square. Z1 5 0 means that the galvanizing content is 1 5 0 grams per square meter, and so on. The number after Z indicates the average coating content at three points on both sides of the galvanized steel in grams per square meter. The general materials of hot-dip galvanizing on the market are: Z80, Z100, Z120, Z140, Z180, Z275, etc. Galvanizing products are widely used in industry, agriculture, animal husbandry and fishery, energy, transportation, chemical industry, light industry, home appliances, construction, communications, national defense and other fields.
Specifications
Product Parameters
| Product Name | DX51D Z150 Galvanized Coil |
| Thickness | 0.12mm-3.5mm |
| Width | 600mm-1500mm |
| Length | 508mm/610mm,Support Customization |
| Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
| Zinc Layer | Hot Galvanizing: 60-275g/m² |
| Pre-galvanized: 80-275g/m² |
Chemical Composition
| Standard | Grade | C | Si | Mn | P | S | Ti |
|---|
| Forcold Forming Chinese Standard | DX51D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX52D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX53D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX54D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX56D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX57D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| Forcold Forming Japanese Standard | SGCC | 0.15 | 0.50 | 0.80 | 0.050 | 0.030 | 0.025 |
| SGCD1 SGCD2 | 0.12 0.10 | 0.50 0.50 | 0.60 0.45 | 0.040 0.030 | 0.030 0.030 | 0.025 0.025 |
| SGCD3 | 0.08 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| SGCD4 | 0.06 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| For Structure Japanese Standard | SGC340 | 0.25 | 0.50 | 1.70 | 0.200 | 0.035 | 0.025 |
| SGC400 SGC440 | 0.25 0.25 | 0.50 0.50 | 1.70 2.00 | 0.200 0.200 | 0.035 0.035 | 0.150 0.150 |
| SGC490 | 0.30 | 0.50 | 2.00 | 0.200 | 0.035 | 0.025 |
| SGC510 | 0.30 | 0.50 | 2.50 | 0.200 | 0.035 | 0.025 |
| For Structure AISI Standard | S220GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S250GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S280GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S320GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S350GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
| S550GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
Mechanical Properties
| Grade | Yield Strength MPa≥ | Tensile Strength MPa≥ | Elongation A%≥ |
|---|
| DX51D Z/ZM/AZ/AM | 240-380 | 270-500 | 22 |
| DX52D Z/ZM/AZ/AM | 140-300 | 270-420 | 26 |
| DX53D Z/ZM/AZ/AM | 140-260 | 270-380 | 30 |
| DX54D Z/ZM/AZ/AM | 120-220 | 260-350 | 36 |
| S220GD Z/ZM/AM | 220 | 300 | 20 |
| S250GD Z/ZM/AZ/AM | 250 | 330 | 19 |
| S280GD Z/ZM/AM | 280 | 360 | 18 |
| S300GD A/AM | 300 | 380 | 18 |
| S320GD Z/ZM/AM | 320 | 390 | 17 |
| S350GD Z/ZM/AZ/AM | 350 | 420 | 16 |
| S450GD A/AM | 450 | 480 | 15 |
| S550GD Z/ZM/AZ/AM | 550 | 550 | - |
Galvanized Surface Selection
| Zero Spangle | Minimized Spangle | Normal Spangle | Large Spangle |
|---|
| | | |
| Use of The Environment | Recommended Zinc Thickness |
|---|
| Indoor Use | Z10 or Z12 (100g/㎡or 120g/㎡) |
| Suburbs | Z20 and Painting (200g/㎡) |
| Urban or Industrial Area | Z27 (270g/㎡) or G90 (US Standard) and painted |
| Coastal Area | Thicker than Z27 (270g/㎡) or G90 (US Standard) and painted |
| Punch or Deep Drawing Application | Thicker than Z27 (270grams/㎡) or G90 (US Standard) avoid coating peeling after stamping |
| Surface Treatment Type | Code | Features |
|---|
| Chromic Acid Treatment | C | Good corrosion resistance,suitable for bare state |
| Chromic Acid Treatment+Oiling | S | Good corrosion resistance |
| Phosphoric Acid Treatment (Including Sealing Treatment) | P | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Including Sealing Treatment)+Oiling | Q | Has a certain corrosion resistance,good paint performance,prevent rust during transportation and storage |
| Phosphoric Acid Treatment (Excluding Sealing Treatment) | T | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Excluding Sealing Treatment)+Oiling | V | Has a certain corrosion resistance,good paint performance,and prevent rust |
| Oiling | O | Prevent rust during transportation and storage |
| No Treatment | M | Suitable for immediate painting |
Material Comparison
| Chinese Standard | Japan Standard | European Standard |
|---|
| DX51D Z/DC51D Z (CR) | SGCC | DX51D Z |
| DX52D Z/DC52D Z | SGCD1 | DX52D With |
| DX53D Z/DC53D Z/DX54D Z/DC54D Z | SGCD2/SGCD3 | DX53D Z/DX54D Z |
| S220/250/280/320/350/550GD Z | SGC340/400/440/490/570 | S220/250/280/320/350GD Z |
| DX51D Z/DD51D Z (HR) | SGHC | DX51D Z |