A588 Pressure Vessel Carbon Steel Coil
SKU: HC-1134549951405338624
A588 alloy structural steel coil is made of a kind of weather-resistant steel, and its material standard is ASTM A588/A588M. It is a type of low-alloy high-strength structural steel and is mainly used for structural components in outdoor exposure environments, such as bridges, large containers, chimneys, etc..
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：haven@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
A588 alloy structural steel coil is made of a kind of weather-resistant steel, and its material standard is ASTM A588/A588M. It is a type of low-alloy high-strength structural steel and is mainly used for structural components in outdoor exposure environments, such as bridges, large containers, chimneys, etc.. A588 alloy structural steel coil not only has high weather resistance to prevent atmospheric corrosion, but also has superior mechanical properties. As a matter of fact, this steel coil can form a protective layer on the surface of the metal substrate through alloying of Cu, P, Cr, Ni, etc., thus having high atmospheric corrosion resistance. A588 alloy structural steel coil has high tensile strength and yield strength at room temperature, as well as good elongation properties. The coils are widely used in structural engineering fields such as bridges, high-rise buildings, towers, and transmission towers. Its weather resistance can provide long-term structural stability and strong resistance to atmospheric corrosion, thus extending the service life of the structure.
Specifications
Product Parameters
| Product Name | A588 Pressure Vessel Carbon Steel Coil |
| Production Process | Hot Rolling,Cold Rolling |
| Material Standards | AISI,ASTM,ASME,DIN,BS,EN,ISO,JIS,GOST,SAE,etc. |
| Width | 45mm-2200mm |
| Length | Custom Size |
| Thickness | Hot Rolling: 2.75mm-100mm Cold Rolling: 0.2mm-3mm |
| Delivery Conditions | Rolling,Annealing,Quenching,Tempered or Standard |
| Surface Process | Ordinary,Wire Drawing,Laminated Film |
Chemical Composition
| A588 | C | Mn | P | S | Si | Ni | Cr | Cu | V |
|---|---|---|---|---|---|---|---|---|---|
| Grade A | 0.19 % | 0.80-1.25 % | 0.03 % | 0.03 % | 0.30-0.65 % | 0.40 % | 0.40-0.65 % | 0.25-0.40 % | 0.02-0.10 % |
| Grade B | 0.20 % | 0.75-1.35 % | 0.03 % | 0.03 % | 0.15-0.50 % | 0.50 % | 0.40-0.70 % | 0.20-0.40 % | 0.01-0.10 % |
| Grade C | 0.17 % | 0.50-1.20 % | 0.03 % | 0.03 % | 0.25-0.50 % | 0.40 % | 0.40-0.70 % | 0.30-0.50 % | - |
Mechanical Properties
| Thickness | Yield Strength (Ksi) | Tensile Strength Min (ksi) | Min. 2 " Elongation % | Min. 8 " Elongation % |
|---|---|---|---|---|
| Below 4 mm | 50 | 70 | 21 | 18 |
| 4in. - 5 in . | 46 | 67 | 21 | - |
| 5in. - 8 in. | 42 | 63 | 21 | - |
Equivalent Material
| American Standard ASTM A588 | ASME SA588 | German Standard DIN,WNr | United Kingdom BS | Italy UNI | European Standard EN |
|---|---|---|---|---|---|
| A588 Grade A | SA588 Grade A | WTSt 52-3 | WR 50 C | Fe 510 D2K1 | S355J2G1W |