Product Description
Galvanized sheet is a type of steel that is coated with zinc for protection by an electroplating process. The galvanized layer is applied to cold rolled steel at low temperatures. So it is also known as cold galvanized steel. Through electrolytic galvanizing, a uniform and dense zinc layer is finally formed on the surface of the steel, but the mechanical properties of the material are still maintained. Electrogalvanized steel is usually sold in coil or sheet form. EG coil is a kind of material that can be cut, slitted and profiled for other purposes. The steel grade of galvanized steel consists of base metal grade, galvanized (E), galvanized layer type and weight. The electro-galvanized products based on SPCC, SPCD, SPCE, SPCF and SPCG are named SECC, SECD, SECE, SECF and SECG respectively. Full Cold Galvanizing Process: Chemical degreasing → hot water washing → water washing → electrolytic degreasing → water washing → acid washing → rust removal → water washing → electrogalvanizing process → water washing → passivation → hot water washing → drying → quality inspection → packaging and sales
Product Parameters
| Product Name | Hot Dip Galvanized Sheet |
|---|
| Thickness | 0.12mm-6.00mm |
| Width | 600mm-1500mm |
| Length | 1m-12m,Support Customization |
| Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
| Zinc Layer | Hot Galvanizing: 60-275g/m² |
| Pre-galvanized: 80-275g/m² |
Chemical Composition
| Standard | Grade | C | Si | Mn | P | S | Ti |
|---|
| Forcold Forming Chinese Standard | DX51D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX52D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX53D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX54D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX56D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX57D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| Forcold Forming Japanese Standard | SGCC | 0.15 | 0.50 | 0.80 | 0.050 | 0.030 | 0.025 |
| SGCD1、SGCD2 | 0.12、0.10 | 0.50、0.50 | 0.60、0.45 | 0.040、0.030 | 0.030、0.030 | 0.025、0.025 |
| SGCD3 | 0.08 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| SGCD4 | 0.06 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| For Structure Japanese Standard | SGC340 | 0.25 | 0.50 | 1.70 | 0.200 | 0.035 | 0.025 |
| SGC400、SGC440 | 0.25、0.25 | 0.50、0.50 | 1.70、2.00 | 0.200、0.200 | 0.035、0.035 | 0.150、0.150 |
| SGC490 | 0.30 | 0.50 | 2.00 | 0.200 | 0.035 | 0.025 |
| SGC510 | 0.30 | 0.50 | 2.50 | 0.200 | 0.035 | 0.025 |
| For Structure AISI Standard | S220GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S250GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S280GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S320GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S350GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
| S550GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
Mechanical Properties
| Grade | Yield Strength MPa≥ | Tensile Strength MPa≥ | Elongation A%≥ |
|---|
| DX51D Z/ZM/AZ/AM | 240-380 | 270-500 | 22 |
| DX52D Z/ZM/AZ/AM | 140-300 | 270-420 | 26 |
| DX53D Z/ZM/AZ/AM | 140-260 | 270-380 | 30 |
| DX54D Z/ZM/AZ/AM | 120-220 | 260-350 | 36 |
| S220GD Z/ZM/AM | 220 | 300 | 20 |
| S250GD Z/ZM/AZ/AM | 250 | 330 | 19 |
| S280GD Z/ZM/AM | 280 | 360 | 18 |
| S300GD A/AM | 300 | 380 | 18 |
| S320GD Z/ZM/AM | 320 | 390 | 17 |
| S350GD Z/ZM/AZ/AM | 350 | 420 | 16 |
| S450GD A/AM | 450 | 480 | 15 |
| S550GD Z/ZM/AZ/AM | 550 | 550 | - |
Galvanized Surface Selection
| Zero Spangle | Minimized Spangle | Normal Spangle | Large Spangle |
|---|
| Use of The Environment | Recommended Zinc Thickness |
|---|
| Indoor Use | Z10 or Z12 (100g/㎡or 120g/㎡) |
| Suburbs | Z20 and Painting (200g/㎡) |
| Urban or Industrial Area | Z27 (270g/㎡) or G90 (US Standard) and painted |
| Coastal Area | Thicker than Z27 (270g/㎡) or G90 (US Standard) and painted |
| Punch or Deep Drawing Application | Thicker than Z27 (270grams/㎡) or G90 (US Standard) avoid coating peeling after stamping |
| Surface Treatment Type | Code | Features |
|---|
| Chromic Acid Treatment | C | Good corrosion resistance,suitable for bare state |
| Chromic Acid Treatment+Oiling | S | Good corrosion resistance |
| Phosphoric Acid Treatment (Including Sealing Treatment) | P | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Including Sealing Treatment)+Oiling | Q | Has a certain corrosion resistance,good paint performance,prevent rust during transportation and storage |
| Phosphoric Acid Treatment (Excluding Sealing Treatment) | T | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Excluding Sealing Treatment)+Oiling | V | Has a certain corrosion resistance,good paint performance,and prevent rust |
| Oiling | O | Prevent rust during transportation and storage |
| No Treatment | M | Suitable for immediate painting |
Material Comparison
| Chinese Standard | Japan Standard | European Standard |
|---|
| DX51D Z/DC51D Z (CR) | SGCC | DX51D Z |
| DX52D Z/DC52D Z | SGCD1 | DX52D With |
| DX53D Z/DC53D Z/DX54D Z/DC54D Z | SGCD2/SGCD3 | DX53D Z/DX54D Z |
| S220/250/280/320/350/550GD Z | SGC340/400/440/490/570 | S220/250/280/320/350GD Z |
| DX51D Z/DD51D Z (HR) | SGHC | DX51D Z |