Product Description
G60 is the coating grade of steel sheet after continuous hot dip plating process. G represents the "galvanized" or galvanized layer of the product. The number 60 refers to the thickness of the zinc around the steel sheet or the thickness of the entire double-sided coating. The coating designation G 6 0 represents the type of coating and the weight of the applied coating. The letter "G" indicates that the coating is galvanized, meaning zinc-based. Meanwhile, the number " 6 0" represents the thickness of zinc on the surface of the steel sheet. Galvanized steel sheets are covered with a zinc coating to provide corrosion resistance. Galvanized steel sheet G60 is coated with molten zinc. After the continuous coating process at a speed of 600 feet per minute, the excess zinc on the steel plate is removed by high-pressure air. This is to produce the desired coating thickness. The G60 protective coating prevents moisture from reaching the steel structure, thereby improving the corrosion resistance of the steel. This can extend the life expectancy of the steel. Galvanizing products are widely used in industry, agriculture, animal husbandry and fishery, energy, transportation, chemical industry, light industry, home appliances, construction, communications, national defense and other fields.
Specifications
Product Parameters
| Product Name | G60 Galvanized Sheet |
| Thickness | 0.12mm-6.00mm |
| Width | 600mm-1500mm |
| Length | 1m-12m,Support Customization |
| Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
| Zinc Layer | Hot Galvanizing: 60-275g/m² |
| Pre-galvanized: 80-275g/m² |
Chemical Composition
| Standard | Grade | C | Si | Mn | P | S | Ti |
|---|
| Forcold Forming Chinese Standard | DX51D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX52D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX53D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX54D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX56D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX57D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| Forcold Forming Japanese Standard | SGCC | 0.15 | 0.50 | 0.80 | 0.050 | 0.030 | 0.025 |
| SGCD1 SGCD2 | 0.12 0.10 | 0.50 0.50 | 0.60 0.45 | 0.040 0.030 | 0.030 0.030 | 0.025 0.025 |
| SGCD3 | 0.08 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| SGCD4 | 0.06 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| For Structure Japanese Standard | SGC340 | 0.25 | 0.50 | 1.70 | 0.200 | 0.035 | 0.025 |
| SGC400 SGC440 | 0.25 0.25 | 0.50 0.50 | 1.70 2.00 | 0.200 0.200 | 0.035 0.035 | 0.150 0.150 |
| SGC490 | 0.30 | 0.50 | 2.00 | 0.200 | 0.035 | 0.025 |
| SGC510 | 0.30 | 0.50 | 2.50 | 0.200 | 0.035 | 0.025 |
| For Structure AISI Standard | S220GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S250GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S280GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S320GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S350GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
| S550GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
Mechanical Properties
| Grade | Yield Strength MPa≥ | Tensile Strength MPa≥ | Elongation A%≥ |
|---|
| DX51D Z/ZM/AZ/AM | 240-380 | 270-500 | 22 |
| DX52D Z/ZM/AZ/AM | 140-300 | 270-420 | 26 |
| DX53D Z/ZM/AZ/AM | 140-260 | 270-380 | 30 |
| DX54D Z/ZM/AZ/AM | 120-220 | 260-350 | 36 |
| S220GD Z/ZM/AM | 220 | 300 | 20 |
| S250GD Z/ZM/AZ/AM | 250 | 330 | 19 |
| S280GD Z/ZM/AM | 280 | 360 | 18 |
| S300GD A/AM | 300 | 380 | 18 |
| S320GD Z/ZM/AM | 320 | 390 | 17 |
| S350GD Z/ZM/AZ/AM | 350 | 420 | 16 |
| S450GD A/AM | 450 | 480 | 15 |
| S550GD Z/ZM/AZ/AM | 550 | 550 | - |
Galvanized Surface Selection
| Zero Spangle | Minimized Spangle | Normal Spangle | Large Spangle |
|---|
| | | |
| Use of The Environment | Recommended Zinc Thickness |
|---|
| Indoor Use | Z10 or Z12 (100g/㎡or 120g/㎡) |
| Suburbs | Z20 and Painting (200g/㎡) |
| Urban or Industrial Area | Z27 (270g/㎡) or G90 (US Standard) and painted |
| Coastal Area | Thicker than Z27 (270g/㎡) or G90 (US Standard) and painted |
| Punch or Deep Drawing Application | Thicker than Z27 (270grams/㎡) or G90 (US Standard) avoid coating peeling after stamping |
| Surface Treatment Type | Code | Features |
|---|
| Chromic Acid Treatment | C | Good corrosion resistance,suitable for bare state |
| Chromic Acid Treatment+Oiling | S | Good corrosion resistance |
| Phosphoric Acid Treatment (Including Sealing Treatment) | P | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Including Sealing Treatment)+Oiling | Q | Has a certain corrosion resistance,good paint performance,prevent rust during transportation and storage |
| Phosphoric Acid Treatment (Excluding Sealing Treatment) | T | Have a certain corrosion resistance,good paint performance |
| Phosphoric Acid Treatment (Excluding Sealing Treatment)+Oiling | V | Has a certain corrosion resistance,good paint performance,and prevent rust |
| Oiling | O | Prevent rust during transportation and storage |
| No Treatment | M | Suitable for immediate painting |
Material Comparison
| Chinese Standard | Japan Standard | European Standard |
|---|
| DX51D Z/DC51D Z (CR) | SGCC | DX51D Z |
| DX52D Z/DC52D Z | SGCD1 | DX52D With |
| DX53D Z/DC53D Z/DX54D Z/DC54D Z | SGCD2/SGCD3 | DX53D Z/DX54D Z |
| S220/250/280/320/350/550GD Z | SGC340/400/440/490/570 | S220/250/280/320/350GD Z |
| DX51D Z/DD51D Z (HR) | SGHC | DX51D Z |