Docol PHS 1800M Hot Formed Steel (PHS)
SKU: HC-1141749850575015936
Docol PHS 1800M hot-formed steel is integrated with a small amount of boron in the alloy to improve hardness. This steel is widely developed for parts made by direct or indirect hot forming in the automotive industry.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：haven@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
Docol PHS 1800M hot-formed steel is integrated with a small amount of boron in the alloy to improve hardness. This steel is widely developed for parts made by direct or indirect hot forming in the automotive industry. Hot-formed steel is a type of steel that changes its structure and properties through thermo-mechanical processing (such as rolling, forging, extrusion, etc.) under high temperature. Hot-formed steel is widely used in automobile, aerospace, shipbuilding and other industries due to their advantages of high strength, good formability, and fatigue resistance. Hot-formed steel is more ductile than cold-formed steel, meaning it can deform under greater bending and tensile conditions and is more difficult to break. Therefore, Docol PHS 1800 M hot-formed steel is suitable for material applications such as structural parts that need to withstand bending and deformation in use. Besides, the weldability of hot-formed steel is better than that of cold-formed steel, so Docol PHS 1800 M hot-formed steel can be joined and assembled more easily.
Specifications
Mechanical Properties
| Steel Grade | Standard | Status | Test Direction | Yield Strength R p0.2 (MPa) | Tensile Strength R m (MPa) | Extension Rate A 80 (%) | Extension Rate A 5 (%) |
|---|---|---|---|---|---|---|---|
| Docol PHS FH 1800 | SSAB | Full hard | T | 970 | 1070 | 4 | - |
| Docol PHS CR1800 | SSAB | Fire after delivery | T | 350 | 500 | 27 | - |
| Docol PHS CR1800 | SSAB | Hot printing | T | 1300 | 1800 | 6 | - |
Chemical Composition
| Brand | C (max %) | Si (max %) | Mn (max %) | P (max %) | S (max %) | Cr (max %) | B (max %) |
|---|---|---|---|---|---|---|---|
| Docol PHS CR 1 800 | 0.27-0.33 | 0.15-0.35 | 1.00-1.45 | 0.025 | 0.010 | 0.35 | 0.0008-0.0050 |