410 stainless steel is a commonly used martensitic stainless steel consisting of iron, carbon, chromium and a small amount of other elements.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
410 stainless steel is a commonly used martensitic stainless steel consisting of iron, carbon, chromium and a small amount of other elements. 410 stainless steel is a type of martensitic stainless steel with 11.5% chromium . 410 stainless steel bars ha ve been quenched, tempered and polished to step up corrosion resistance. Unlike austenitic stainless steel, martensitic stainless steel is not as superior , which is why martensitic stainless steel requires a final heat treatment before manufacturing . This steel is hardened for maximum resistance to corrosion and heat. 410 stainless steel bars are a versatile and popular manufacturing parts in automotive manufacturing due to its many advantages. High strength is a key advantage making it ideal for applications requiring durability and wear resistance.
Product Parameters
| Product Name | 410 Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10",Thickness: 2mm-150mm,Can provide customized | |
| Length | 1-6 meters,Length can be customized | |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. | |
| Surface | Black,Bright Polished,Rough Turning,Mattness Surface Treatment,No.4. BA,etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding,Defense,Automotive,Textiles,Paper and pulp,Manufacturing,Cement,Heavy earthmoving equipment and construction,etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.15 | ≤ 1.0 | ≤ 1.0 | 11.5～13.5 | ≤ 0.5 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 450 | ≥ 205 | ≥ 20 | ≤ 201HB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 7.74 | 200 | 9.9 | 24.9 | 570 |