410 Stainless Steel Coil
SKU: HC-1128986542856159232
410 stainless steel is a commonly used martensitic stainless steel whose main components are iron, carbon, chromium and a small amount of other elements.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：haven@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
410 stainless steel is a commonly used martensitic stainless steel whose main components are iron, carbon, chromium and a small amount of other elements. 410 stainless steel is a type of martensitic stainless steel with a chromium content of 11.5% to realize excellent corrosion resistance. 410 stainless steel has been quenched, tempered and polished to improve corrosion resistance. And quenching and tempering just makes 410 stainless steel harder. Compared to austenitic stainless steel, martensitic stainless steel is relatively inferior, which is why martensitic stainless steel requires a final heat treatment to be manufactured. Grade 410 stainless steel has the ability to withstand hot gases, steam, food, weak acids and bases, fresh water, and dry air. This steel is hardened for maximum corrosion and heat resistance. A key advantage of this material is its high strength, making it ideal for applications requiring durability and wear resistance.
Specifications
Product Parameters
| Product Name | 410 Stainless Steel Coil |
| Type | Steel Coil |
| Thickness | 2.5mm-10.0mm |
| Length | 2000mm,2440mm,3000mm,5800mm,6000mm,etc. |
| Width | 610mm-2000mm |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. |
| Surface | BA,2B,NO.1,NO.4,4K,HL,8K,etc. |
| Scope of Application | Widely used in high temperature and electrical industry,medical equipment construction,chemical,food industry,agriculture and ship parts,food and beverage packaging,Kitchen supplies,trains,airplanes,conveyor belts,vehicles,bolts,nuts,springs and screens,etc. |
| Certificate | ISO,SGS,BV,etc. |
| Production Technology | Hot Rolling,Cold Rolling |
| Edge Processing | Edging,Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.15 | ≤ 1.0 | ≤ 1.0 | 11.5～13.5 | ≤ 0.5 | ≤ 0.03 | ≤ 0.04 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 450 | ≥ 205 | ≥ 20 | ≤ 201HB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 7 .74 | 200 | 9.9 | 24.9 | 570 |