ASTM A588 steel is sorted into Class A, Class B, Class C, and Class K. The ASTM A588 steel specification is based on the standard specification for high-strength low-alloy structural steel with a lower yield point of up to 50ksi for applications requiring high strength and corrosion resistance.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
ASTM A588 steel is sorted into Class A, Class B, Class C, and Class K. The ASTM A588 steel specification is based on the standard specification for high-strength low-alloy structural steel with a lower yield point of up to 50ksi for applications requiring high strength and corrosion resistance. A588 carbon steel coil shows good corrosion resistance after a special treatment . It is resistant to corrosion of the atmosphere, sea water, and salt spray, thus extending its service life. For another, A588 carbon steel coil is made of high-strength steel that has high yield strength and tensile strength, which can meet the requirements of various structural parts. The coil also has good welding performance, making it easy to weld and process, and therefore improving the efficiency of engineering installation. A588 carbon steel coils are suitable for various structural parts that require corrosion resistance and high strength.
Product Parameters
| Product Name | A588 Carbon Steel Coil |
| Production Process | Hot Rolling,Cold Rolling |
| Material Standards | AISI,ASTM,ASME,DIN,BS,EN,ISO,JIS,GOST,SAE,etc. |
| Width | 45mm-2200mm |
| Length | Custom Size |
| Thickness | Hot Rolling: 2.75mm-100mm Cold Rolling: 0.2mm-3mm |
| Delivery Conditions | Rolling,Annealing,Quenching,Tempered or Standard |
| Surface Process | Ordinary,Wire Drawing,Laminated Film |
Chemical Composition
| A588 | C | Mn | P | S | Ni | Si | Cr |
|---|---|---|---|---|---|---|---|
| Grade A | ≤ 0.19 | 0.80 - 1.25 | ≤ 0.04 | ≤ 0.05 | ≤ 0.40 | 0.30 - 0.65 | 0.40 - 0.65 |
| Grade B | ≤ 0.20 | 0.75 - 1.35 | ≤ 0.04 | ≤ 0.05 | ≤ 0.50 | 0.15-0.50 | 0.40 - 0.70 |
| Grade C | ≤ 0.15 | 0.80 - 1.35 | ≤ 0.04 | ≤ 0.05 | 0.25~0.50 | 0.15-0.40 | 0.30 - 0.50 |
| Grade K | ≤ 0.17 | 0.50 - 1.20 | ≤ 0.04 | ≤ 0.05 | ≤ 0.40 | 0.25-0.50 | 0.40 - 0.70 |
Mechanical Properties
| A588 | Tensile Strength | Yield Strength | Elongation 200 mm % | Elongation 50 in % |
|---|---|---|---|---|
| Thickness ≤ 100 mm | 485 | 345 | 18 | 21 |
| Thickness > 100-125 mm | 460 | 315 | - | 21 |
| Thickness > 125-200 mm | 435 | 290 | - | 21 |
Physical Performance
| Physical Performance | Metric | Imperial |
|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ |