A514 Carbon Steel Plate
SKU: HC-1134508618854674432
ASTM A514 steel is available in several grades: A, B, C, E, F, H, J, K, M, P, Q, S, and T, all of which have the same mechanical properties. ASTM A514 steel plates are conventionally quenched and tempered steel. ASTM A514 steel plate is known for its high yield strength, weldability and toughness. ASTM A514 steel is a special high-strength steel, mainly used as building structural steel.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
ASTM A514 steel is available in several grades: A, B, C, E, F, H, J, K, M, P, Q, S, and T, all of which have the same mechanical properties. ASTM A514 steel plates are conventionally quenched and tempered steel. ASTM A514 steel plate is known for its high yield strength, weldability and toughness. ASTM A514 steel is a special high-strength steel, mainly used as building structural steel. A514 steel plate is a high-strength low-alloy steel plate. Its main components include carbon (C), silicon (Si), manganese (Mn), phosphorus (P), sulfur (S), chromium (Cr), and nickel (Ni). , molybdenum (Mo), vanadium (V) and other elements. The characteristic of A514 steel plate is that it has extremely high strength and toughness, and can obtain higher strength through heat treatment. A514 steel plates are usually used in machinery manufacturing fields that need to withstand high pressure or high temperature environments. A514 steel plates are widely used in petrochemical, aerospace, nuclear industry, military and offshore platforms. In addition, A514 steel plate has good weldability and processability, and is also suitable for construction, bridges and other fields.
Product Parameters
| Product Name | A514 Carbon Steel Plate |
| Production Process | Hot Rolling,Cold Rolling |
| Material Standards | AISI,ASTM,ASME,DIN,BS,EN,ISO,JIS,GOST,SAE,etc. |
| Width | 100mm-3000mm |
| Length | 1m-12m,or Customized Size |
| Thickness | 0.1mm-400mm |
| Delivery Conditions | Rolling,Annealing,Quenching,Tempered Or Standard |
| Surface Process | Ordinary,Wire Drawing,Laminated Film |
Chemical Composition
| A514 | C | Mn | P | S | Ni | Cr | Mo |
|---|---|---|---|---|---|---|---|
| Grade A | 0.15 - 0.21 | 0.80 - 1.10 | 0.035 | 0.4-0.8 | - | 0.5-0.8 | 0.18-0.28 |
| Grade B | 0.12-0.21 | 0.70-1.0 | 0.035 | 0.20-0.35 | - | 0.4-0.65 | 0.15-0.25 |
| Grade C | 0.1-0.2 | 1.10-1.5 | 0.035 | 0.15-0.30 | - | - | 0.15-0.30 |
| Grade E | 0.12-0.20 | 0.4-0.7 | 0.035 | 0.2-0.4 | - | 1.40-2.0 | 0.4-0.6 |
| Grade F | 0.1-0.2 | 0.60-1.0 | 0.035 | 0.15-0.35 | 0.70-1.0 | 0.4-0.65 | 0.4-0.6 |
| Grade H | 0.12-0.21 | 0.95-1.3 | 0.035 | 0.20-0.35 | 0.3-0.7 | 0.4-0.65 | 0.2-0.3 |
| Grade J | 0.12-0.21 | 0.45-0.7 | 0.035 | 0.20-0.35 | - | - | 0.50-0.65 |
Mechanical Properties
| A514 | Thickness mm | Yield Strength Min Mpa | Tensile Strength Mpa | Elongation Rate Min% |
| 20 | 690 | 760-895 | 18 | |
| 20-65 | 690 | 760-895 | 18 | |
| 65-150 | 620 | 690-895 | 18 |
Physical Performance
| Physical Performance | Metric | Imperial |
|---|---|---|
| Density | 7.85 g/cm3 | 0.284 lb/in³ |