303 Stainless Steel Bar
SKU: HC-1109168236787908608
303 stainless steel bar is made of an austenitic, easy-cutting, wear-resistant acid stainless steel containing sulfur and selenium respectively. It is used in situations where cutting and high surface finish are needed.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
303 stainless steel bar is made of an austenitic, easy-cutting, wear-resistant acid stainless steel containing sulfur and selenium respectively. It is used in situations where cutting and high surface finish are needed. 303 stainless steel bars are easy to perform cold and hot processing owing to good plasticity and toughness. They do not easily crack during processing and can meet the processing needs of complex shapes. Such bars can still maintain good toughness and strength in low temperature environments and is suitable for applications that need to deal with low temperature environments. Besides, 303 stainless steel bars can still maintain high strength and good fatigue resistance at high temperatures. As a general-purpose stainless steel type, 303 stainless steel bars can apply to a wide range of things. They are a common manufacturing part in the food industry, chemical industry, petroleum, pharmaceutical and other fields to meet different needs.
Product Parameters
| Product Name | 303 Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10",Thickness: 2mm-150mm,Can provide customized | |
| Length | 1-6 meters,Length can be customized | |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. | |
| Surface | Black,Bright Polished,Rough Turning,Mattness Surface Treatment,No.4. BA,etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding,Defense,Automotive,Textiles,Paper and pulp,Manufacturing,Cement,Heavy earthmoving equipment and construction,etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.15 | ≤1.0 | ≤ 2.0 | 17.0～19.0 | 8.0～10.0 | ≥ 0.15 | ≤ 0.20 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 520 | ≥ 205 | ≥ 40 | ≤ 187HB ; ≤ 90HRB ; ≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(10 -6 * Ω.m) |
|---|---|---|---|---|
| 8.03 | 193 | 17.3 | 16.3 | 0.72 |