310S Stainless Steel Bar
SKU: HC-1131637486480764928
310S stainless steel has incredible oxidation resistance and corrosion resistance as an austenitic chromium-nickel stainless steel. Because of a higher percentage of chromium and nickel, so that it possesses better creep strength as well as high temperature resistance.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
310S stainless steel has incredible oxidation resistance and corrosion resistance as an austenitic chromium-nickel stainless steel. Because of a higher percentage of chromium and nickel, so that it possesses better creep strength as well as high temperature resistance. 310S stainless steel bar has great performances in terms of oxidation resistance, corrosion resistance, acid and alkali resistance given its high content of nickel and chromium . A fter increasing the content of carbon in a ustenitic stainless steel, the strength is improved because of its solid solution strengthening effect. The chemical composition of a ustenitic stainless steel mainly features chromium and nickel , with extra molybdenum, tungsten, niobium and titanium . With a face-centered cubic structure, it has better strength and creep strength at high temperatures. 310S stainless steel bars are commonly adopted as manufacturing parts in the production of boiler, steam turbine, industrial furnace and aviation, petrochemical.
Product Parameters
| Product Name | 310S Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10",Thickness: 2mm-150mm,Can provide customized | |
| Length | 1-6 meters,Length can be customized | |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. | |
| Surface | Black,Bright Polished,Rough Turning,Mattness Surface Treatment,No.4. BA,etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding,Defense,Automotive,Textiles,Paper and pulp,Manufacturing,Cement,Heavy earthmoving equipment and construction,etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.08 | ≤1.0 | ≤ 2.0 | 24.0～26.0 | 19.0～22.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 520 | ≥ 205 | ≥ 40 | ≤ 217HB;≤ 95HRB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 9.01 | 200 | 14.4 | 13.8 | 94 |