316Ti is a titanium stabilized version of 316 molybdenum-containing austenitic stainless steel. It has better resistance to general corrosion and pitting/crevice corrosion than traditional chromium-nickel austenitic stainless steels such as 304.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
316Ti is a titanium stabilized version of 316 molybdenum-containing austenitic stainless steel. It has better resistance to general corrosion and pitting/crevice corrosion than traditional chromium-nickel austenitic stainless steels such as 304. 316Ti stainless steel bars are highly resistant to various corrosive media such as acids, alkalis, and salts primarily because of their high chromium and nickel content . A certain amount of titanium is added to the steel to improve corrosion resistance by creating a stable passivation film. 316Ti stainless steel has good processing properties, such as weldability, bending formability and machining performance. This enables easy processing and connection during the manufacturing process, thus boosting production efficiency. What is more, 316Ti stainless steel bar can be used in the temperature range of -253 ° C to 400 ° C without causing harm to its strength and stability. This makes it widely used in high-temperature settings as manufacturing parts.
Product Parameters
| Product Name | 316Ti Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10",Thickness: 2mm-150mm,Can provide customized | |
| Length | 1-6 meters,Length can be customized | |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. | |
| Surface | Black,Bright Polished,Rough Turning,Mattness Surface Treatment,No.4. BA,etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding,Defense,Automotive,Textiles,Paper and pulp,Manufacturing,Cement,Heavy earthmoving equipment and construction,etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo | Ti |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.08 | ≤1.0 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 | 0.5～0.7 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 515 | ≥ 205 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 7.99 | 193 | 16.0 | 16.2 | 74 |