316L Stainless Steel Coil
SKU: HC-1128980583488372736
316L stainless steel features a lower proportion of carbon in its composition. The amount of carbon cannot be higher 0.03%. This lowers the risk of carbon precipitation, making it a better option for welding to achieve maximum corrosion resistance.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
316L stainless steel features a lower proportion of carbon in its composition. The amount of carbon cannot be higher 0.03%. This lowers the risk of carbon precipitation, making it a better option for welding to achieve maximum corrosion resistance. 3 16 L stainless steel coil is a variant of 3 16 stainless steel coil with a lower carbon content and it is used mostly for welding purposes . The lower carbon content minimizes the precipitation of carbides in the heat-affected zone close to the weld, and the precipitation of carbides may cause intergranular corrosion of stainless steel in certain environments. Basically, using 316L eliminates the need to anneal weld joints prior to using the completed metal form, saving time and effort. 316L stainless steel coil is one of the most widely used stainless steel like 304, and its corrosion resistance is better than 304. High temperature resistance is also better, up to 1000 degrees. 316L stainless steel is a kind of universal stainless steel material, with stronger rust resistance than 200 series stainless steel material.
Product Parameters
| Product Name | 316L Stainless Steel Coil |
| Type | Steel Coil |
| Thickness | 2.5mm-10.0mm |
| Length | 2000mm,2440mm,3000mm,5800mm,6000mm,etc. |
| Width | 610mm-2000mm |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. |
| Surface | BA,2B,NO.1,NO.4,4K,HL,8K,etc. |
| Scope of Application | Widely used in high temperature and electrical industry,medical equipment construction,chemical,food industry,agriculture and ship parts,food and beverage packaging,Kitchen supplies,trains,airplanes,conveyor belts,vehicles,bolts,nuts,springs and screens,etc. |
| Certificate | ISO,SGS,BV,etc. |
| Production Technology | Hot Rolling,Cold Rolling |
| Edge Processing | Edging,Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo |
|---|---|---|---|---|---|---|---|
| ≤ 0.03 | ≤1.0 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 480 | ≥ 177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 7.99 | 193 | 16.0 | 16.2 | 74 |