305 Stainless Steel Plate
SKU: HC-1109081283066630144
305 stainless steel is a common austenitic stainless steel containing elements such as chromium, nickel, and manganese. Chromium is the main anti-corrosion element and can combine with oxygen to form a dense oxide film to protect materials from corrosion. Nickel can improve the material's heat resistance and toughness while reducing its magnetism. Manganese can increase the strength and hardness of materials.
Key Features
- ✓Third-Party Inspection Support
- ✓Sufficient Inventory Supply
- ✓International Standard Certification
- ✓Custom Processing Service
Contact Us
- Phone：+86 15052357278
- Email：juniper@hongchen-steel.com
- WhatsApp：+86 15052357278
Scan to chat
Product Description
305 stainless steel is a common austenitic stainless steel containing elements such as chromium, nickel, and manganese. Chromium is the main anti-corrosion element and can combine with oxygen to form a dense oxide film to protect materials from corrosion. Nickel can improve the material's heat resistance and toughness while reducing its magnetism. Manganese can increase the strength and hardness of materials. 305 stainless steel has good corrosion resistance and can remain stable in various corrosive media. The oxide film formed on its surface can effectively prevent the contact between the corrosive medium and the material, thereby extending the service life of the material. 305 stainless steel has good heat resistance and can maintain stable performance at high temperatures. Its high content of nickel element can improve the heat resistance of the material, making it less likely to deform, oxidize or fail at high temperatures. In addition, it has high strength and hardness and can withstand greater pressure and impact. Its high content of manganese element can improve the strength and hardness of the material, making it less likely to deform or break when under pressure. 305 stainless steel is often used in the chemical industry, food processing, construction, aerospace, marine engineering, and other fields.
Product Parameters
| Product Name | 305 Stainless Steel Plate |
| Type | Plate |
| Thickness | 0.3mm-200mm |
| Length | 2000mm,2438mm,3000mm,5800mm,6000mm,12000mm,etc. |
| Width | 40mm-600mm,1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,3000mm,3500mm,etc. |
| Standard | ASTM,AISI,JIS,GB,DIN,EN,etc. |
| Surface | BA,2B,NO.1,NO.4,4K,HL,8K,etc. |
| Scope of Application | Widely used in high temperature and electrical industry,medical equipment construction,chemical,food industry,agriculture and ship parts,food and beverage packaging,Kitchen supplies,trains,airplanes,conveyor belts,vehicles,bolts,nuts,springs and screens,etc. |
| Certificate | ISO,SGS,BV,etc. |
| Production Technology | Hot Rolling,Cold Rolling |
| Edge Processing | Edging,Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.04 | ≤ 0.75 | ≤ 2.0 | 17.0～19.0 | 10.5～13.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥ 515 | ≥ 205 | ≥ 35 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10 -6 /°C) | Coefficient of Thermal Conductivity(W/m * K) | Resistivity(ΜΩ. cm) |
|---|---|---|---|---|
| 7.99 | 193 | 17.3 | 16.2 | 72 |